Nickel Alloy Inconel 600 Plate Thickness 0.5 - 30.0mm Alloy 600 Sheet According to ASTM SB168 B
| Products Name | Inconel 600 Nickel Alloy Sheet Plate |
| Thickness | Cold rolled: 0.5 - 3.0mm Hot rolled 4.0 - 30.0mm |
| Standard Size | 1000*2000mm 1219*2438mm 1219*3048mm 1500*6000mm |
| Surface | 2B NO.1 |
| MOQ | 50 kgs |
| Service | Cutting, Surface Finishing |
| Packing | Waterproof paper and wooden pallets |
| Loading Port | Shanghai Port |
| Price term | FOB CFR CIF EXW |
| Payment term | 30% TT in advance , 70% TT balance against copy of B/L |
| Other Grade | Hastelloy C22 C4 X C276 |
| Monel 400 K500 |
| Incoloy 800 800H 800HT 825 925 |
| Inconel 600 601 625 716 718 |
| Stainless Steel Grade | 201 202 301 304L 309S 310S 316L 316Ti 317L 321 347 409L 410 410S 420J1 420J2 430 431 436L 439 440A/B/C 441 443 444 2205 2507 904L 254SMO 253MA |
Alloy 600 is a nonmagnetic, nickel-based high temperature alloy possessing an excellent combination of high strength, hot and cold workability, and resistance to ordinary form of corrosion.
This alloy also displays good heat resistance and freedom from aging or stress corrosion throughout the annealed to heavily cold worked condition range.
Applications of Inconel 600 Niickel Alloy Sheet
Some typical applications are:
- Barge and tank truck liners
- Carburizing atmospheres
- Ethylene dichloride crackers
- Furnace trays, mufflers, hangers
- Gasoline stabilizer production
- MgCl2 evaporates
- Phenol condensers
- Soap manufacture
- Titanium dioxide
- Vegetable and fatty acid vessels
Corrosion Resistance of Inconel 600
The high chromium content of alloy 600 raises its oxidation resistance considerably above that of pure nickel, while its high nickel content provides good corrosion resistance under reducing conditions.
This alloy exhibits high levels of resistance to stress and salt water, exhaust gases, and most organic acids and compounds.
Heat Treatment of Inconel 600
Alloy 600 is not an age hardening alloy; cold working is the only available means of hardening. Softening by annealing begins at about 1600°F (871°C), and is reasonably complete after 10 to 15 minutes of heating at 1800°F (982°C). Above this temperature, grain growth may be objectionable, although very brief heating at 1900°F will cause complete softening without undue grain growth. Since the rate of cooling has no effect on the softening, the material may be water quenched or air cooled.
Workability of Inconel 600
Hot Working/Forging
Low sulfur reducing furnace atmospheres should be used in forging. Major hot working should be done between 2300/1850°F, while light working may be continued as low as 1600°F. No hot working should be attempted between 1600/1200°F due to lower ductility in that range.
Machinability
Alloy 600 is machinable in both the hot worked and annealed conditions. Because considerable heat is generated in machining this alloy, high-speed steel, cast nonferrous or cemented carbide tools should be used. The tools should be kept sharp.
Lathe turning speeds with high-speed and nonferrous tools are 35/45 sfm (0.18/0.23 m/s); speeds with cemented carbide tools are 100/175 sfm (0.51/0.89 m/s). (This data should be used as a guide for initial machine setup only. The figures used are averages. On certain work, the nature of the part may require adjustment of speeds and feeds.)
Sulfur-based oil should be used as a lubricant, but should be completely removed before the machined part is exposed to elevated temperatures, as in welding.
Cold Working
For higher properties, alloy 600 can be cold worked below 1200°F (649°C).
Welding
Alloy 600 can be joined by the usual welding , brazing, and soldering process.
Typical Mechanical Properties of Alloy 600
Typical Mechanical Properties
Various forms and conditions
Form
and
Condition | Tensile Strength | 0.2%
Yield Strength | % Elongation
in 2" | %
Reduction
of Area | Rockwell
Hardness |
Rod and Bar
Cold-drawn
Annealed
As-drawn
Hot rolled
Annealed
As-rolled
Hot-finished
Strip
Annealed |
80-100
105-150
80-100
85-120
80-120
80-100 |
552-689
724-1034
552-689
586-827
586-827
552-689 |
25-50
80-125
30-50
35-90
35-90
30-45 |
172-345
552-862
207-345
241-621
241-621
207-310 |
55-35
30-10
55-35
50-30
50-30
55-35 |
70-60
60-30
70-60
65-50
65-50
---- |
65-85B
90B-30C
65-85B
75-95B
75-95B
84B max. |
Average Room Temperature Tensile Data
| Form | Condition | Ultimate Tensile Strength,
Ksi (MPa) | Yield Strength at 0.2% offset,
Ksi (MPa) | Elongation in 2 in. (50.8mm)
or 4D, percent |
Sheet
Plate
Bar/Billet
Sheet, Plate, Strip, Bar | Annealed
Annealed
Annealed
Annealed | 98 (676)
95 (655)
95 (655)
80 (550)* | 42 (290)
41 (283)
41 (283)
35 (240)* | 40
45
45
30* |
|
|
Nickel Alloy Inconel 600 Plate Thickness 0.5 - 30.0mm Alloy 600 Sheet According to ASTM SB168 B Images
|